In the use of welding tools to carry out welding operations, in the process of steel welding, there are still steel cold cracking phenomenon. There are many reasons for this situation, which are generally related to the chemical composition, steel degree, preheating temperature and cooling conditions of steel. In order to appear the phenomenon of the maximum limit underground steel cold crack, we must pay attention to the following technical points:
First of all, for steel welding, attention should be paid to the moisture in welding materials, rust, oil stain at the groove of welding parts, and environmental humidity. In general, the amount of hydrogen in the base metal and welding wire is very small, but the moisture in the electrode coating and the moisture in the air can not be ignored and become the main source of hydrogen enrichment.
The solubility of hydrogen in austenite is much higher than that in ferrite. Therefore, the solubility of hydrogen decreases suddenly when the austenite changes to ferrite during welding. At the same time, the diffusion rate of hydrogen is just opposite, and increases suddenly when it changes from austenite to ferrite.
Finally, a large amount of hydrogen will be dissolved in the molten pool under the action of high temperature during welding. In the subsequent cooling and condensation process, due to the sharp decrease of solubility, hydrogen is trying to escape. However, due to the rapid cooling, hydrogen is retained in the weld metal to form diffusion hydrogen.
This article comes from the manual welding equipment of water tankhttp://www.frankiejohn.com
Methods to reduce welding deformation and control
I. causes and types of welding deformation causes of welding deformation: welding deformation refers to the deformation of weldments during and after welding. During welding, the molten metal and the base metal near the seam expand and produce plastic deformation. During solidification, the weld and the metal near the seam contract. This is the longitudinal stress and the transverse stress. Make the weld longitudinal and transverse shrinkage, so that the weldment deformation. Because the heat e
Specific differences between grinding machine and polishing machine
Difference: the workpiece processed by grinding machine is rough, and the surface finish of workpiece processed by polishing machine is better, but high finish can be achieved by installing precise grinding wheel on grinding machine. Grinding machine: electric grinder reciprocating electric polishing grinder (also known as file mill). It is widely used in the fine machining and surface polishing of the mold profession. It is a substitute for similar pneumatic products. The main outstanding featu
How to improve the efficiency of straight seam welding machine?
The straight seam welding machine is widely used in ordinary times, and our appeal to the seam welding machine is constantly strengthened. We should know about the operation of the seam welding machine. The straight seam welding machine is not only excellent in spot welding machine, but also excellent in seam welding machine. A good machine must be equipped with a good operator. It is not simple to be a good operator. In addition to the accumulation of time experience, it also needs many tips, s
How to deal with the failure of welding robot?
General welding robot factory has the following shortcomings: a) human shortcomings caused by improper operation, mainly including welding gun damage in welding robot factory, improper loading and unloading of workpieces, and no deformation of positioner follow-up. B) the disadvantages of poor design and manufacture of peripheral equipment mainly include: problems of lifting way switch and cable, quality problems of some components flashed by teaching device. C) improper environmental protection